CYCOLOY™ CS9610 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKGPb8_CYCOLOYCS9610resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior. This grade potentially can be considered for a wide variety of applications in areas such as transportation, consumer electronics and electrical equipments. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 62.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 4.8 | % | ISO 527-2/50 |
| Fracture 5 | 55 | % | ASTM D638 |
| Fracture | > 45 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2440 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 98.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 10 | 15 | kJ/m² | ISO 180/1A |
| 23°C 11 | 45 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 118 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 106 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 124 | °C | ISO 306/B50 |
| -- | 127 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.0 mm) | V-0 5VB | UL 94 | |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, Dmax | 225 | ASTM E662 | |
| Flaming, Ds, 1.5 min | 40.0 | ASTM E662 | |
| Flaming, Ds, 4 min | 150 | ASTM E662 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 260 - 300 | °C | |
| Middle Temperature | 260 - 300 | °C | |
| Front Temperature | 265 - 300 | °C | |
| Nozzle Temperature | 265 - 300 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60 - 90 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 50A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Niretan B S25 AE/V0 | Soredi S.p.a. | Nylon 6 | Niretan B |
| ChronoPrene™ 15A | AdvanSource Biomaterials Corp. | TPE | ChronoPrene™ |
| Karina BLACK PVC COMPOUND 800-48/1-CY-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OXPEKK® C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |