Hylex® P1003L2 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YIBvam_HylexP1003L2HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCARBONATE, BRANCHED, LOW MELT FLOW |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 62.1 | MPa | ASTM D638 |
| Fracture, 23°C | 64.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 7.0 | % | ASTM D638 |
| Fracture, 23°C | > 70 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP213G20 | Kolon Plastics, Inc. | PBT | SPESIN® |
| Abstron KU650N | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Karina COMP. PVC IVORY 80800-35/ 1-C-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ DP003 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Hostacom TRC 104N C12628 | LyondellBasell Industries | PP Copolymer | Hostacom |