Elastollan® B 60 D
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YHrnV8_Elastollan-B-60-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, good tensile strength, good damping and resilience performance and superior low temperature flexibility. Typical applications Sport-shoe soles and accessories, Skiboot shells, technical mouldings, e.g. seals, castor tyres, tubing. Certain UV stabilised B grades are available on request |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 60 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 240 | MPa | ISO 527-2 |
| Abrasion Loss | 25.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 20% Strain | 13.0 | MPa | |
| 100% Strain | 16.0 | MPa | |
| 300% Strain | 30.0 | MPa | |
| Tensile Stress | DIN 53504 | ||
| Yield 1 | 40.0 | MPa | |
| Yield | 55.0 | MPa | |
| Tensile Elongation | DIN 53504 | ||
| Break 2 | 450 | % | |
| Break | 500 | % | |
| Tear Strength 3 | 150 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 35 | % | |
| 70°C, 24 hr | 45 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | No Break |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® PA1350 | SAMBARK | Nylon, Unspecified | SUPRAN® |
| EQUATE PE EFDC-7050 | EQUATE Petrochemical Company KSCC | LLDPE | EQUATE PE |
| KOPLA PA66 KUG1330BK | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| KumhoSunny ABS H2938Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Sylvin 8240-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |