Eastman™ 13319
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Eastman™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YHnn2d_Eastman-13319.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman™ Copolyester 13319 has a high melting point, low extractables, and good hydrolytic stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| -- 1 | 1.20 | g/cm³ | ASTM D1505 |
| -- 2 | 1.21 | g/cm³ | ASTM D1505 |
| Apparent Density (Poured) | 0.74 | g/cm³ | ASTM D1895 |
| Intrinsic Viscosity | |||
| 23°C 3 | 0.96 | ||
| Film : 23°C, 125.0 µm | 0.84 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fusion heat (23°C) | 67.0 | kJ/kg | ASTM E793 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 4 | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Elastic Modulus - MD (25 µm) | 2280 | MPa | ASTM D882 |
| Tensile Strength - MD (Break, 25 µm) | 145 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | 30 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 25 | g | ASTM D1922 |
| TD : 25 µm | 20 | g | ASTM D1922 |
| Oxygen Permeability (23°C, 25 µm, 50% RH) | 21 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (23°C, 50% RH, 25 µm) | 2.3 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 92.0 | °C | DSC |
| Peak Melting Temperature | 285 | °C | ASTM D3418 |
| Specific Heat | DSC | ||
| 50°C | 1500 | J/kg/°C | DSC |
| 130°C | 1800 | J/kg/°C | DSC |
| 180°C | 2000 | J/kg/°C | DSC |
| 250°C | 2200 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.21 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 109 | ASTM D2457 | |
| Transmittance (regular, 25.0 µm) | 91.0 | % | ASTM D1003 |
| Haze (25.0 µm) | 4.2 | % | ASTM D1003 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density (300°C) | 1.09 | g/cm³ | ASTM D1238 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 299 - 316 | °C |
| Injection instructions |
|---|
| Drying Dew Point: -29 to -40°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 299 - 302 | °C |
| Extrusion instructions |
|---|
| Drying Dew Point: -29 to -40°C |
| Note Message | |
|---|---|
| 1 . | Amorphous |
| 2 . | Film |
| 3 . | EMN-A-AC-G-V-1 |
| 4 . | Film-to-Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXTEL® 600T10-BK | MRC Polymers, Inc. | PP, Unspecified | MAXTEL® |
| SUSTAMID 12 | Röchling Sustaplast SE & Co. KG | Nylon 12 | SUSTAMID |
| Toraycon® 1101G-X50 | Toray Resin Company | PBT | Toraycon® |
| Nymax™ ND 1233 GF Natural | PolyOne Corporation | Nylon 66 | Nymax™ |
| Karina BLACK PVC COMPOUD -E CAK 85-48/ 1-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |