Nypol® PA B3 G30 LRJ0319 NT368
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YHmaQv_Nypol-PA-B3-G30-LRJ0319-NT368.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 in color orange, reinforced with 30% glass fiber, lubricated, ideal for injection molding, good set of thermal properties, electrical and mechanical. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 to 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 | % | ASTM D570 |
| Ash Content | 28 to 32 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 7900 | MPa | ASTM D790 |
| Flexural Strength | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648 |
| Vicat Softening Temperature | 210 | °C | ASTM D1525 1 |
| Melting Temperature | 210 to 225 | °C | ASTM D2117 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPA66 GF 30 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | Nylon 66 | RC Plastics |
| Salflex 364A | Salflex Polymers Ltd. | TPV | Salflex |
| Baoding 6126H | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| HIPOLEN P® MA 31 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| Huafon JF-A-AH2060 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |