Novalloy-B B27B6
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YHhEQb_Novalloy-B-B27B6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novalloy-B B27B6 is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 8140 | MPa | ASTM D790 |
| Flexural Strength | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 190 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 121 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.483 to 1.45 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9703-66 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nipol® IR 2200 | Zeon Corporation | IR | Nipol® IR |
| Karina CLEAR CRYSTAL PVC COMP. -E 85/201-DA-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EPAMOULD 685A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |