ELIX™ 5120
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ELIX Polymers, S. L. |
| Trademark: | ELIX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YHddll_ELIX-5120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS blend, injection molding grade with excellent mechanical properties balance up to -40°C. Vicat B120 = 120°C Benefits:
Chemical Composition:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | |||
| Across Flow | 0.65 to 0.75 | % | ISO 294-4 |
| Flow | 0.65 to 0.75 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.70 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2320 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 28 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2320 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 30 | kJ/m² | |
| -30°C | > 27 | kJ/m² | |
| 23°C | > 38 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.2E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3 | < 80 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Velocity | 40 | mm/sec | ISO 294 |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm |
| 2 . | 2.0 mm/min |
| 3 . | 150x105x1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 732 CS A/B | Wacker Chemie AG | Silicone | POWERSIL® |
| Next Nylon 6 Prime Series NXF-01WH | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| DENYL 66 3010 | Vamp Tech | Nylon 66 | DENYL |
| Evermore PUR SA-230P | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| ALTECH® PA6 + ASA A 4010/212 MR10 IM UV | ALBIS PLASTIC GmbH | Nylon 6+ASA | ALTECH® PA6 + ASA |