Durethan® DP 2131/20 W1 901317
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YGvGid_Durethan-DP-2131-20-W1-901317.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 20 % glass fibers, injection molding, weather stabilized, improved surface finish |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 260°C, 3.00 mm 1 | 0.67 | -- | % | |
| Across Flow : 120°C, 4 hr, 3.00 mm 2 | 0.20 | -- | % | |
| Flow : 260°C, 3.00 mm 3 | 0.22 | -- | % | |
| Flow : 120°C, 4 hr, 3.00 mm 4 | 0.070 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 198 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7600 | 4700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 6400 | 4100 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 197 | 110 | MPa | |
| 23°C 6 | 212 | 130 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.1 | 6.4 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHLR, 14-080, GF20 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | -- | kJ/m² | |
| 23°C | < 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 45 | 60 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 30 | 30 | kJ/m² | |
| 23°C | 30 | 40 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 4.00 | -- | J | |
| 23°C | 5.00 | 10.0 | J |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 213 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 73.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 9 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.3E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.9E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 2.0E+15 | 2.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 3.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.10 | 9.34 | ||
| 23°C, 1 MHz | 3.74 | 4.27 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 8.0E-3 | 0.22 | ||
| 23°C, 1 MHz | 0.018 | 0.065 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 500 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 500 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-010 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| VESTAKEEP® Film 0FH80 | Evonik Industries AG | PEEK | VESTAKEEP® Film |
| Vikalloy IM62 | Viking Polymers, LLC | PMMA+PVC | Vikalloy |
| Hanwha Total PP TB53H | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, HMS | Hanwha Total PP |
| Shida 101 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |