Generic Nylon 66/6 - Glass Fiber
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YGh1My_Generic-Nylon-66-6---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66/6 - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 - 1.70 | g/cm³ | ASTM D792 |
| 23°C | 1.20 - 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 0.65 | % | ASTM D955 |
| 23°C | 0.10 - 0.91 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.35 - 1.8 | % | ASTM D570 |
| 23°C, 24 hr | 0.63 - 5.8 | % | ISO 62 |
| Saturated, 23°C | 5.0 - 8.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 - 2.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 84 - 85 | ISO 868 | |
| Ball Indentation Hardness | 160 - 274 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5200 - 16800 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 80.0 - 250 | MPa | ISO 527-2 |
| Fracture, 23°C | 110 - 242 | MPa | ISO 527-2 |
| 23°C | 143 - 174 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 2.0 - 3.0 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 5.1 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 4.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4230 - 9520 | MPa | ASTM D790 |
| 23°C | 5440 - 9110 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 130 - 291 | MPa | ASTM D790 |
| 23°C | 144 - 286 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.9 - 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 29 - 95 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 43 - 160 | J/m | ASTM D256 |
| 23°C | 2.9 - 16 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 39 - 51 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 224 - 256 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 - 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 199 - 253 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 60.0 - 176 | °C | ISO 75-2/C |
| Continuous Use Temperature | 100 - 230 | °C | ASTM D794 |
| Vicat Softening Temperature | 195 - 241 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 260 | °C | ISO 11357-3 |
| -- | 242 - 262 | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 - 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 65.0 - 67.1 | °C | UL 746 |
| RTI Imp | 65.0 - 66.1 | °C | UL 746 |
| RTI | 65.0 - 67.1 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+12 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 21 - 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.56 | IEC 60250 | |
| Comparative Tracking Index | 442 - 605 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 - 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.0 - 80.0 | °C | |
| Drying Time | 2.9 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 - 0.21 | % | |
| Rear Temperature | 259 - 270 | °C | |
| Middle Temperature | 258 - 296 | °C | |
| Front Temperature | 255 - 290 | °C | |
| Processing (Melt) Temp | 255 - 298 | °C | |
| Mold Temperature | 60.0 - 93.0 | °C | |
| Injection Pressure | 79.5 - 99.0 | MPa | |
| Holding Pressure | 50.7 - 97.5 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66/6 - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7868-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ASTAGLAS™ MV825I | Marplex Australia Pty. Ltd. | Acrylic (PMMA) | ASTAGLAS™ |
| Cellophane™ 600MSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Elastane™ 4721R10 | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Infino ASF-9810F | SAMSUNG SDI CO., LTD. | PBT+PET | Infino |