Ultramid A3L HP is an unreinforced, heat stabilized, impact modified, high flow, nylon 66 for injection molding. This grade has excellent flow and improved ambient and low temperature toughness. Applications Typical applications include fasteners and clamps. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2440 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 63.5 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 6.2 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 28 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 19 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 12 | kJ/m² | |
| 23°C | 18 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.040 to 0.20 | % | |
| Processing (Melt) Temp | 288 to 305 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 40 to 80 | rpm | |
| Screw Compression Ratio | 3.0:1.0 to 4.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P grey homopolymer | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| SPESIN® KP212G15V0BM | Kolon Plastics, Inc. | PBT | SPESIN® |
| TAROMID A 280 G5 Y0 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Durepol® PBT A3 G20 PRTA011 BT321 MSP | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| GAPEX® RPP30EB22NA | Ferro Corporation | PP Homopolymer | GAPEX® |