LNP™ THERMOTUF™ VF008 compound
| Category: | Nylon 66 , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YFDWhS_LNPTHERMOTUFVF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* VF008 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound VF-1008 Product reorder name: VF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 131 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 9650 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 890 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 245 | °C | ASTM D648 |
| CLTE - Flow (-40 to 40°C) | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.38 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 - 271 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 293 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Regis® 6200 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| Desmopan® 588 E | Covestro - PUR | TPU-Ester/Ether | Desmopan® |
| Gallonprene® GP420-6002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HIFOR Xtreme® SC74845 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| Sylvin 5175-92 White 1476 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |