SABIC® PPcompound 8536
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YEyBPg_SABIC-PPcompound-8536.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8536 is a development grade, elastomer-modified mineral filled Polypropylene for painted automotive exterior applications. This material has been designed to combine a good performance profile with good processing. SABIC® PPcompound 8536 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.50 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 18.5 | MPa | |
| Break, 3.20 mm, Injection Molded | 13.5 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | > 150 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 10 | kJ/m² | |
| 0°C, Injection Molded | 60 | kJ/m² | |
| 23°C, Injection Molded | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.5E-5 | cm/cm/°C | |
| 23 to 80°C | 6.5E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 92682 E | RTP Company | Nylon 6 | RTP |
| THERMOLAST® K TP0LDZ (Series: UV/LD/b) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Nanjing Hongrui PC CT306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| Borealis PP BF335SA | Borealis AG | PP Copolymer | Borealis PP |
| Cheng Yu N6GV3 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |