Order Products : sales@su-jiao.com
Cleapact TI-300S
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | DIC Corporation |
| Trademark: | Cleapact |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YETV3r_Cleapact-TI-300S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Developed with our unique polymerization technology, Cleapact is a type of styrene copolymer resin that excels in the balance of transparency, shock-resistance and molding capacity. Products in this category have a variety of positive characteristics and meet diverse range of user needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.70 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 68 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Injection Molded | 49.0 | MPa | |
| Break, Injection Molded | 32.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 15 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 2450 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.0 | °C | ISO 306 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Injection Molded) | 89.0 | % | JIS K7105 |
| Haze (Injection Molded) | 3.0 | % | JIS K7105 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 2550®B-CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| SCANTEC PC S60R GF30 | Polykemi AB | PC | SCANTEC |
| Evoprene™ GC 5650 | AlphaGary | SEBS | Evoprene™ GC |
| Desmovit® DP R 9929 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| FHR Polypropylene P9G8Z-036 | Flint Hills Resources, LP | PP, Unspecified | FHR Polypropylene |