NYCOA Polyamide ASN 27 440 KNF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YEQt8I_NYCOA-Polyamide-ASN-27-440-KNF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA ASN 27/440 KNF is a 44% glass fiber reinforced, heat stabilized Nylon 6 resin used for injection molding. This resin was engineered for applications requiring high stiffness, and toughness. NYCOA ASN 27/440 KNF is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. Typical applications include automotive pedals, weed trimmer heads, and speaker brackets. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 | % | ASTM D955 |
| Transverse flow | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11900 | MPa | ASTM D638 |
| Tensile Strength 2 | 240 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 4 | 13100 | MPa | ASTM D790 |
| Flexural Strength 5 | 280 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 243 - 282 | °C | |
| Front Temperature | 254 - 291 | °C | |
| Nozzle Temperature | 252 - 291 | °C | |
| Processing (Melt) Temp | 254 - 291 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PRC25TF3.2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| API PS 505 | American Polymers, Inc. | PS (HIPS) | API PS |
| Geon™ Vinyl Flexible XV3830 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| INSULCAST® 116 FR-FC-FS | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| Karina IVORY PVC COMPOUND 808D35/ 1-DY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |