| Nylon 66, 15% Glass Filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 121 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 5170 | MPa | ISO 178 |
| Flexural Stress | 179 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 235 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ SY 89-21-1 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Nypol® PA A3 ST HS UV5 PRTA011 NR427 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| EVALENE® LLDPE LF20185 | JG Summit Petrochemical Corporation | LLDPE | EVALENE® LLDPE |
| EMOPLEN® HP MCF 30 | EMAS Plastik San.Tic.AS. | PP Homopolymer | EMOPLEN® |
| ENGAGE™ 7277 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |