EVAL™ F171
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YECBdP_EVAL-F171.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
32 mol% Ethylene Vinyl Alcohol Copolymer F171A - non-lubricated pellets F171B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.6 | g/10 min | |
| 210°C/2.16 kg | 3.7 | g/10 min | |
| Ethylene Content | 32.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 5.9E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 7.9E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 1.3 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 57.0 | °C | ISO 11357-2 |
| Melting Temperature | 183 | °C | ISO 11357 |
| Peak Crystallization Temperature | 158 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3967H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Texalan® 5 Series 595A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| VITAMIDE® BR36BK6613 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| CERTENE™ 1320 | Muehlstein | PS (HIPS) | CERTENE™ |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |