HIPLEX® TR 130
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YC5boQ_HIPLEX-TR-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPLEX® TR-130, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties. Applications: HIPLEX® TR-130 is suitable for production of advertising bags, industrial bags, bags for food package, and for production of composite films and blends with other kind of polyethylene. HIPLEX® TR-130 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX® TR-130 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.18 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 18.0 | MPa | |
| Break | 32.0 | MPa | |
| Tensile Strain (Break) | 900 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 24.0 | MPa | |
| TD : Yield, 25 µm | 19.0 | MPa | |
| MD : Break, 25 µm | 43.0 | MPa | |
| TD : Break, 25 µm | 33.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 550 | % | |
| TD : Break, 25 µm | 700 | % | |
| Dart Drop Impact (25 µm) | 88 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.0 µm | 42.5 | kN/m | |
| TD : 25.0 µm | 251.0 | kN/m |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature 2 | 195 to 220 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ISO 306 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blow-up ratio: 3.5-5 : 1, Neck height: 6-10 times die diameter |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH 810HF | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| ELASTOSIL® LR 3043/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| K-Flex EL 37 FR | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| KPOL-NYLON K-NY66/21VC | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |
| KRATON® D4433 P | Kraton Polymers LLC | SIS | KRATON® |