Hylex® P1310G30FRMA
| Category: | PC , Polycarbonate |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YBhmns_Hylex-P1310G30FRMA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, 30% Glass Filled, Flame Retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 6800 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 148 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AG7H | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Stanyl® 46HF5050 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Ultramid® B3WG6 BK00564 BGVW | BASF Corporation | Nylon 6 | Ultramid® |
| Karina IVORY PVC COMPOUND -E 800-35/ 1-Y-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Magnobond 104-228 | Magnolia Plastics, Inc. | Epoxy | Magnobond |