SEPAZ™ C245GP
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YB6D8w_SEPAZ-C245GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ C245GP is a Liquid Crystal Polymer (LCP) product filled with 45% glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.050 | % | |
| Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.90 | % | ASTM D638 |
| Flexural Modulus | 18300 | MPa | ASTM D790 |
| Flexural Strength | 191 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 295 | °C | ASTM D648 |
| Peak Melting Temperature | 352 | °C | ASTM D2133 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant | 4.30 | ASTM D150 | |
| Dissipation Factor | 0.025 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 360 to 370 | °C | |
| Mold Temperature | 30.0 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOMAMID® 66G30HUV | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Hytrel® PC966 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Lumid® GP1300AP | LG Chem Ltd. | Nylon 6 | Lumid® |
| LUVOCOM® 80-7917 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| PERLER® B39V4000A01 | A.D. Compound S.p.A. | PP Homopolymer | PERLER® |