HiFill® PET GF20 UV BK
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YAO1eF_HiFill-PET-GF20-UV-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PET GF20 UV BK is a Polyethylene Terephthalate (PET) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 114 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 246 | °C | |
| 1.8 MPa, Unannealed | 224 | °C | |
| CLTE - Flow | 9.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 271 to 288 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 271 to 288 | °C | |
| Processing (Melt) Temp | 274 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-85A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Tenite™ Propionate 360A4000012 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| XENOY™ CL500U resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| Dryflex® 4097-002 | ELASTO | TPO (POE) | Dryflex® |
| OLEFISTA™ QX0238B | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |