Network Polymers PP 30 0500 GF40
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Network Polymers PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y9zQI4_Network-Polymers-PP-30-0500-GF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Network Polymers PP 30 0500 GF40 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 40% glass fiber. It is available in North America. Primary characteristic: chemically coupled. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 0.318 mm, Injection Molded) | 0.18 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break, 23°C, 3.18 mm, Injection Molded) | 106 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.18 mm, Injection Molded) | 2.8 | % | ASTM D638 |
| Flexural Modulus - Tangent 4(23°C, 3.18 mm, Injection Molded) | 7980 | MPa | ASTM D790 |
| Flexural Strength 5(23°C, 3.18 mm, Injection Molded) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm, Injection Molded) | 162 | °C | ASTM D648 |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 40 | % | ASTM D2584 |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 216 V35 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Spartech Polycom SC14-2090 | Spartech Polycom | Nylon 6 | Spartech |
| Moplen RP5007K | PolyMirae | PP Random Copolymer | Moplen |
| ULTEM™ 2310EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Laprene® 83FM00A90 | SO.F.TER. SPA | SEBS | Laprene® |