LNP™ LUBRICOMP™ RFN18S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y8qY9Y_LNPLUBRICOMPRFN18Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RFN18S is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4218 HS Product reorder name: RFN18S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.1 | % | ASTM D955 |
| Lateral flow : 24 hours | 1.2 | % | ISO 294-4 |
| Traffic : 24 hours | 0.35 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.62 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15500 | MPa | ASTM D638 |
| -- | 14000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 178 | MPa | ASTM D638 |
| Fracture | 192 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.8 | % | ASTM D638 |
| Fracture | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10800 | MPa | ASTM D790 |
| -- | 13100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 268 | MPa | ASTM D790 |
| -- | 288 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| Dynamic | 0.75 | ASTM D3702 Modified | |
| Static | 0.59 | ASTM D3702 Modified | |
| Wear Factor - Washer | 45.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 890 | J/m | ASTM D4812 |
| 23°C 3 | 59 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.70 | J | ASTM D3763 |
| -- | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 259 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 251 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | > 240 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ AG511 | Asahi Kasei Chemicals Corporation | Nylon+PPE | XYRON™ |
| Caltex PP H550 | GS Caltex | PP Homopolymer | Caltex PP |
| DOW™ VLDPE DFDB-1085 NT | The Dow Chemical Company | VLDPE | DOW™ VLDPE |
| Sylvin 83028-90 Orange 5112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX830 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |