S-RIM™ 6261 Tan
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | S-RIM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y8mOFO_S-RIM-6261-Tan.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
S-RIM™ 6261 Tan is a Thermoplastic product. It can be processed by structural react. inject. molding (srim) and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D2566 |
| Weight - per cubic inch | 18 | g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 655 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 17 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 11 | J/m | ASTM D256 |
| Unnotched Izod Impact | 62 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed 2 | 189 | °C | |
| 0.45 MPa, Unannealed 3 | 108 | °C | |
| 1.8 MPa, Unannealed 4 | 157 | °C | |
| 1.8 MPa, Unannealed 5 | 117 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 85, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 600 | cP | ASTM D4878 |
| Demold Time (21°C) | 5.0 to 12 | min | Internal Method |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | post cured at 140°C |
| 3 . | post cured at 80°C |
| 4 . | post cured at 140°C |
| 5 . | post cured at 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA6 D61 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Moplen HP325M | LyondellBasell Industries | PP Homopolymer | Moplen |
| COSMOPLENE® AZ564 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| ExxonMobil™ PP7033L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| LNP™ STAT-KON™ 115EM4 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ STAT-KON™ |