AMTOPP BA25
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Inteplast Group |
| Trademark: | AMTOPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y8AuEF_AMTOPP-BA25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
General Purpose CoEx Heat Sealable BIAXIALLY ORIENTED POLYPROPYLENE FILM TWO SIDE SEALABLE FOR FOOD PACKAGING |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Dimensional Stability | |||
| Across Flow, 130°C 1 | < 3.0 | % | |
| Flow, 130°C 2 | < 5.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 117 | MPa | |
| TD : Yield | 207 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 190 | % | |
| TD : Break | 70 | % | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 5.4 | g/m²/24 hr | ASTM F1249 |
| Yield 3 | 44.1 | m²/kg |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Seal Temperature 4 | |||
| Treated Side | 121 | °C | |
| Untreated side | 104 | °C | |
| Surface Energy | 38 | dyne/cm | ASTM D2578 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 85 | ASTM D2457 | |
| Haze | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 5 minuites |
| 2 . | 5 minutes |
| 3 . | Internal Method |
| 4 . | 1/2 sec, 30 PSI |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3183 | RTP Company | PFA | RTP |
| TAIRIPRO T8002 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| BMC 3001H | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| CELEX™ 500S2 | Trinseo | PC+ABS | CELEX™ |
| Latamid 66 | LATI S.p.A. | Nylon 66 | Latamid |