LNP™ LUBRICOMP™ WL0049 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y82Krf_LNP-LUBRICOMP-WL0049-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WL0049 is a compound based on PBT containing 20% PTFE. Added features include: Wear Resistant, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound WL0049 Product reorder name: WL0049 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 120 | MPa | ASTM D638 |
| -- | 2530 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 42.0 | MPa | ISO 527-2/5 |
| Break 2 | 2.00 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 2.9 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2500 | MPa | ASTM D790 |
| -- 6 | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 74.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.11 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -1.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 2.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256 |
| 23°C 8 | 2.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 290 | J/m | ASTM D4812 |
| 23°C 9 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.50 | J | ASTM D3763 |
| -- | 1.12 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 134 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 79.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 243 to 260 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP5610 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| UNIVAL™ DMDG-6240 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| Gallonprene® GP210-8504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Dynacom 504-G30 | Dynachem Co. Ltd. | ABS | Dynacom |
| INEOS PP 100-CA50 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |