LNP™ LUBRICOMP™ ZL003 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y6oOmh_LNP-LUBRICOMP-ZL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZL003 is a compound based on PPE+PS resin containing 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound ZL-4030 Product reorder name: ZL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.87 | % | ISO 294-4 |
| Flow : 24 hr | 0.83 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Break | 46.9 | MPa | ASTM D638 |
| Break | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 8.5 | % | ASTM D638 |
| Yield | 8.1 | % | ISO 527-2 |
| Break | 8.9 | % | ASTM D638 |
| Break | 8.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 75.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.28 | ||
| vs. Itself - Static | 0.20 | ||
| Wear Factor - Washer | 11.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 3.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 3 | 17 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 130 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 118 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 119 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris POM FW716CS | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| SUPREME Specialty PS SP6411 1924 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| THERMOLAST® K TF7BTL (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Nypol® PA B3 G25 NTLA010 NT337 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| LEXAN™ 3413HF resin | SABIC Innovative Plastics | PC | LEXAN™ |