DOW™ LDPE 955I

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Y5h36X_DOW-LDPE-955I.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Low Density Polyethylene (LDPE)

Typical applications include lids, caps/closures, general purpose

Excellent clarity

Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1.

Complies with U.S. FDA -DMF.

Complies with U.S. USP

Complies with Canadian HPFB No Objection (With Limitations)

Complies with EU, No 10/2011

Consult the regulations for complete details.

DOW Polyethylene 955I Low Density is a medium molecular weight distribution homopolymer designed to offer excellent clarity and flexibility and good toughness with low warpage. This resin has good processability over a wide range of molding conditions.

General Information
Agency Ratings	DMF not rated FDA 21 CFR 177.1520(c) 2.1 HPFB (Canada) No Objection 2 USP Not Rated Europe No 10/2011
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.923	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	35	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50)	< 1.00	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	45		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	9.65	MPa	ASTM D638
Fracture	6.89	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.0	%	ASTM D638
Fracture	90	%	ASTM D638
Flexural Modulus - 2% Secant	296	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength ¹	252	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	38.9	°C	ASTM D648
Brittleness Temperature	-40.0	°C	ASTM D746
Vicat Softening Temperature	95.0	°C	ASTM D1525
Melting Temperature (DSC)	112	°C	Internal method
Peak Crystallization Temperature (DSC)	96.1	°C	Internal method

Additional Information
根据 ASTM D 4976 进行基板模制和测试。

Note Message
1 .	Type s

Resin Grade	Manufacturer	Category	Trademark
SCHULAFORM® 9 E HI	A. Schulman Europe	Acetal (POM) Copolymer	SCHULAFORM®
apilon 52c® C 80	API SpA	TPU-Polyester	apilon 52c®
Appeel® 20D867	DuPont Packaging & Industrial Polymers	EA	Appeel®
ELASTICHEM™ 5511TX-02	Colorite Polymers	PVC, Flexible	ELASTICHEM™
TechnoElast V D5000 I 2 se	TechnoCompound GmbH	TPE	TechnoElast