VECTRA® E463i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y4zVC5_VECTRA-E463i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
40% glass/mineral filled excellent flow, low warpage, high heat resistance. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 all colors at 1.5mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130°C, mechanicals 130°C. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.38 | % | ISO 294-4 |
| Flow direction | 0.050 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 44 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 10600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 130 | MPa | ISO 178 |
| Compressive Modulus | 7700 | MPa | ISO 604 |
| Compressive Stress (1% Strain) | 53.0 | MPa | ISO 604 |
| Flexural Strain at Break | 3.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 270 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 185 | °C | ISO 306/B50 |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 59 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 3.5E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 325 - 335 | °C | |
| Front Temperature | 330 - 350 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 335 - 345 | °C | |
| Mold Temperature | 80.0 - 130 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 150 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 335 to 355°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BSR 30 | Arkema | Nylon 11 | Rilsan® |
| SPESIN® KP213G30SB3 | Kolon Plastics, Inc. | PBT | SPESIN® |
| Moplen HP520H | LyondellBasell Industries | PP Homopolymer | Moplen |
| COSMOPLENE® FY4012E | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Homopolymer | COSMOPLENE® |
| PENTAMID A L1 H black | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |