Leona™ 1702
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y38WZm_Leona-1702.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 1702 is a Polyamide 66 (Nylon 66) product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 1702 include engineering/industrial parts, film and sheet. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.3 to 2.0 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 2.5 | % | |
| Equilibrium, 23°C, 50% RH | -- | 2.5 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 80 | 55 | ||
| R-Scale | 120 | 105 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1100 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield, 23°C | 84.0 | 50.0 | MPa | ISO 527-2 |
| -- | 80.0 | 59.0 | MPa | ASTM D638 |
| Tensile Strain | ||||
| Yield, 23°C | 4.5 | 27 | % | ISO 527-2 |
| Break | 100 | 300 | % | ASTM D638 |
| Break, 23°C | -- | > 100 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 2800 | 1200 | MPa | ASTM D790 |
| 23°C | 2800 | 900 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 118 | 54.0 | MPa | ASTM D790 |
| 23°C | 115 | 39.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 4.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | 28 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 49 | 250 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 230 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | -- | J/kg/°C | |
| Thermal Conductivity | 0.20 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 20 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Oxygen Index | 23 | -- | % | ASTM D2863 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND AU 5100 | POLY GIN | PC | MARCOBLEND |
| Mecoline S RDX 1216 F | Melos GmbH | TP, Unspecified | Mecoline |
| Teflon® FEP CJ 95 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| Elastollan® 565 A P | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| LIHAN® A9705P | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |