Borealis PP HK030U
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y2GBdY_Borealis-PP-HK030U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HK030U is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection moulding process as well as in combination with LGF concentrates on the injection moulding process. The product is available in standard black 9502. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 350 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 72.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 1550 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1450 | MPa | ISO 178 |
| Flexural Stress | 43.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 0.80 | kJ/m² | |
| -20°C | 0.90 | kJ/m² | |
| 23°C | 1.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 11 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 1.6 | kJ/m² | |
| 23°C | 1.8 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 91.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A |
| -- | 89.0 | °C | ISO 306/B |
| CLTE - Flow (-30 to 80°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5145-90 CLEAR YELLOW 4112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2900-95 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Moplen HP520H | LyondellBasell Industries | PP Homopolymer | Moplen |
| Durepol® PBT A3 FR NTLA010 BT329 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| INEOS HDPE K44-11-128 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |