ACCUTECH™ CP0436C30L1
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y25BOH_ACCUTECH-CP0436C30L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0436C30L1 is a polypropylene copolymer (PP Copoly) product, which contains a 30% calcium carbonate filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 62 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 19.0 | MPa | ASTM D638 |
| Fracture | 15.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Flexural Strength | 25.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 52.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 91.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Nylon 101 | Quadrant Engineering Plastic Products | Nylon 66 | Quadrant EPP |
| Adell Polyamide BL-18 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| AKROMID® B3 GF 30 S3 natural (2984) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Formolene® 5100J | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| TORZEN® G2500HS1L NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |