Braskem PE PB-681
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y1pALI_Braskem-PE-PB-681.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: The PB681 is a resin produced under high pressure, in tubular reactor. This resin presents excellent 'draw down'(stability to form fine films). The films produced with this resin present excellent optical properties. Applications: LLDPE and HDPE blends. Process: Blown Film Extrusion Cast Film Extrusion Injection Moulding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 30.0 | MPa | ASTM D882 |
| TD : Fracture | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 370 | % | ASTM D882 |
| TD : Fracture | 1100 | % | ASTM D882 |
| Dart Drop Impact | 60 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD | 100 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 120 | ASTM D2457 | |
| Haze | 4.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 5.00 - 25.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 110 | °C | |
| Die Temperature | 150 | °C |
| Extrusion instructions |
|---|
| Blown FilmScrew L/D relation: 16 to 30:1Compression rate: 3 to 4:1Screen package(Mesh): 40/60/40From the screw to the die: 140°CBlow up ratio: 2 to 3:1Frostline height: at most equivalent to the bubble diameterCast FilmScrew L/D relation: at least 20:1Screw: 180 to 250°CDie: 250 to 290°CChill roll: 40°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 50 H TS | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Unichem 7011LT-03 | Colorite Polymers | PVC, Unspecified | Unichem |
| 4MID® 9A20000 H | 4Plas | Nylon 66 | 4MID® |
| Polifor® 12 CA/30 BIANCO 0179 X1 | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Amphora™ 3D Polymer AM3300 | Eastman Chemical Company | Unspecified | Amphora™ |