ULTEM™ 9075 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XzZ341_ULTEM9075resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 2.4 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3310 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 85 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3240 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 100mm span | 145 | MPa | ASTM D790 |
| Fracture, 100mm span | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 2100 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 35.3 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 189 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 6 | SECT A-1 | FAR 25.853 | |
| Halogen Content | 0 | Internal method | |
| OSU total heat release 7 | 10.0 | kW·min/m² | FAR 25.853 |
| Vertical Burn Test | FAR 25.853 | ||
| Test a (60 s), passes at | 1.0 | sec | FAR 25.853 |
| Test b (12 s), passes at | 0.0 | sec | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 338 - 360 | °C | |
| Middle Temperature | 343 - 366 | °C | |
| Front Temperature | 349 - 371 | °C | |
| Nozzle Temperature | 349 - 371 | °C | |
| Processing (Melt) Temp | 349 - 371 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 100 | °C | |
| Cylinder Zone 1 Temp. | 280 - 300 | °C | |
| Cylinder Zone 2 Temp. | 295 - 320 | °C | |
| Cylinder Zone 3 Temp. | 305 - 330 | °C | |
| Cylinder Zone 4 Temp. | 310 - 335 | °C | |
| Adapter Temperature | 285 - 335 | °C | |
| Melt Temperature | 295 - 330 | °C | |
| Die Temperature | 275 - 330 | °C | |
| Calibration Temp, First | 140 - 170 | °C | |
| Calibration Temp, Second | 90.0 - 130 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Method A/B |
| 7 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 360E2R30016 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| TORZEN® G3500HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Delta PPO FR1G41 | Delta Polymers | PPE+PS | Delta |
| Karina BLACK PVC COMPOUND 70900-48/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TOTAL Polyethylene Lumicene® M 4040 (Pipe) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |