3M™ Dyneon™ Fluoroelastomer FE 5530

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XwQZbW_3MDyneonFluoroelastomerFE5530.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

3M™ Dyneon™ Fluoroelastomer FE 5530 is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. FE 5530 has an incorporated bisphenol cure system.

Special Features

Composition: Low fluorine content terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene

Good compression set resistance

Clean running with excellent mould release

Process target: injection and transfer moulding

Improved low temperature flexibility over standard dipolymers and terpolymers

Proprietary incorporated cure technology

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5530 is ideal for automotive fuel system and oil seal applications, especially O-ring seals for fuel injection systems.

General Information
Features	Low compressive deformability Terpolymer Good demoulding performance
Uses	O-rings Seals Application in Automobile Field
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Resin transfer molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	42	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	71		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	5.20	MPa	ASTM D412A
Tensile Strength ²	15.4	MPa	ASTM D412A
Tensile Elongation ³(Break)	220	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	18	%	ASTM D1414
200°C, 70 hr ⁵	17	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
Verolloy S1230	PlastxWorld Inc.	PC+ABS	Verolloy
ExxonMobil™ SFT315	ExxonMobil Chemical	PP Homopolymer	ExxonMobil™
Kynar Flex® 3121-50	Arkema	PVDF	Kynar Flex®
INSTRUC PA612GF20	Infinity LTL Engineered Compounds	Nylon 6/12	INSTRUC
Karina CLEAR PVC COMPOUND -E 80/266-IS-RG	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina