InnoPlus LD2420D
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XuVW1p_InnoPlus-LD2420D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| InnoPlus LD2420D is produced by high pressure tubular process, a technology licensed by LyondellBasell. This grade offers easy processability, good balance of mechanical and optical properties. Film extruded from InnoPlus LD2420D has high tensile strength, elongation, good toughness and good tear strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 240 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 10.0 | MPa | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 24.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 18.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 320 | % | |
| TD : Break, 70 µm, Blown Film | 550 | % | |
| Dart Drop Impact (70 µm, Blown Film) | 200 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 70.0 µm, Blown Film) | > 20 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | < 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 46GP009UV | Reliance Industries Limited | HDPE | RELENE® |
| Celstran庐 PEHD-GF40-01 | Celanese Corporation | HDPE | Celstran® |
| Karina NATURAL PVC COMPOUND 900-25/ 1-AYR-IS-LMP (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8864-70D White 1445 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| UBESTA 3030XA | UBE America, Inc. | Nylon 12 | UBESTA |