Jam 15YF8
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Jam Petrochemical Company |
| Trademark: | Jam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XsGS8x_Jam15YF8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
15YF8 is a hexane HP-LLDPE blown film grade for high performance applications. This resin processes easier than conventional LLDPEs and has low gels. Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.77 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness | 18.0 - 180 | µm |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm, blown film | 190 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm, blown film | 220 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 12.5 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 13.4 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 35.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 33.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 860 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 170 | g | ASTM D1922 |
| TD : 25 µm, blown film | 510 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 45 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 18 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® S 3268 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Chemiton GBC0NA 70R | Franplast S.r.l. | SEEPS | Chemiton |
| Edgetek™ PI-40GF/000 BLACK | PolyOne Corporation | PEI | Edgetek™ |
| ElectriPlast® EP-CF/PP | Integral Technologies, Inc. | PP, Unspecified | ElectriPlast® |
| Kuraray R-Polymer R-2105 | Kuraray Co., Ltd. | PVOH | Kuraray R-Polymer |