Vipel® K022-CCL-00
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xs5RTZ_Vipel-K022-CCL-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel Fire Retardant Bisphenol A, Epoxy Vinyl Ester Resin AOC's Vipel K022 series is a brominated bisphenol A epoxy vinyl ester resin dissolved in styrene. Vipel K022 series is ideally suited for use in hand lay-up, spray-up, filament winding and pultrusion processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. Vipel K022-CN series contains antimony products. Fire Retardant Some Vipel K022 versions do not require antimony trioxide to meet ASTM E 84 Class I flame spread requirements. Mechanical Properties Vipel K022 is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Versatile Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Corrosion Resistance Vipel K022 is highly resistant to a number of chemical environments. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Bound Styrene | 44.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 40 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| 25°C, Cast | 3590 | MPa | |
| 66°C, Cast | 3010 | MPa | |
| 93°C, Cast | 2860 | MPa | |
| 121°C, Cast | 883 | MPa | |
| 135°C, Cast | 13.1 | MPa | |
| Tensile Strength | ASTM D638 | ||
| 25°C, Cast | 83.0 | MPa | |
| 66°C, Cast | 68.3 | MPa | |
| 93°C, Cast | 49.6 | MPa | |
| 121°C, Cast | 8.27 | MPa | |
| 135°C, Cast | 1.45 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, 25°C, Cast | 5.4 | % | |
| Break, 66°C, Cast | 5.1 | % | |
| Break, 93°C, Cast | 6.1 | % | |
| Break, 121°C, Cast | > 10 | % | |
| Break, 135°C, Cast | 12 | % | |
| Flexural Modulus (25°C, Cast) | 3650 | MPa | ASTM D790 |
| Flexural Strength (25°C, Cast) | 143 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Cast) | 112 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Spread | 30.0 | ASTM E84 | |
| Smoke Developed | 563 | ASTM E84 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 25.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel to Peak | 15.0 | min | |
| Peak Exotherm | 185 | °C | |
| Thixotropic Index | 2.00 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life | 13 | wk | |
| Thermoset Mix Viscosity 2(25°C) | 500 | cP | ASTM D2393 |
| Note Message | |
|---|---|
| 1 . | with 1.25% MEKP |
| 2 . | Brookfield LV viscosity spindle 3 at 60 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 14CGF40-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Fortron® 6345L4 | Celanese Corporation | PPS | Fortron® |
| Kuraray R-Polymer R-3109 | Kuraray Co., Ltd. | PVOH | Kuraray R-Polymer |
| Braskem PP F013M | Braskem America Inc. | PP Homopolymer | Braskem PP |
| Sylvin 6416-70 Blue 8438 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |