Vydyne® R413
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XrDz6Z_Vydyne-R413.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R413 is general-purpose, impact-modified, 13% glass-fiber reinforced PA66 resin. Available in natural, It is specifically designed to maximize toughness, while retaining physical properties. This product is also lubricated for improved flow and offers superior surface appearance. Glass-fiber reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Typical Applications/End Uses: Vydyne R413 is successfully used in a wide range of injection-molding engineering applications, including automotive clips, fasteners, brackets and carbon canisters; electrical connectors, housings, bobbins, etc.; and industrial gears, bearing shells, covers, housings, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.21 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.80 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.70 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5500 | 4100 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 110 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | 13 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4800 | 2800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | 73.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 5.0 | 5.0 | kJ/m² | |
| -30°C | 6.0 | 10 | kJ/m² | |
| 23°C | 12 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 80 | 70 | kJ/m² | |
| 23°C | 75 | 76 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 9.0 | 9.0 | kJ/m² | |
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 21 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH5GF2-7894 Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Chemical Resources GPPS0600REP | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| Electrafil® J-1200/CF/15/V0/ND BK2089 | Techmer Engineered Solutions | ABS | Electrafil® |
| Delas 180 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PVC+NBR | Delas |
| NORYL™ NH4030B resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |