DOW™ LDPE 545E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XqZ9yb_DOW-LDPE-545E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE™ 545E is 0.9 melt index, medium density LDPE suitable for collation shrink film application offering a good balance between shrink performance (hot and cold shrink), optical properties such as high gloss and low haze and mechanical performance. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.40 to 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm | 215 | MPa | |
| 2% Secant, TD : 50 µm | 222 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 12.0 | MPa | |
| TD : Yield, 50 µm | 13.0 | MPa | |
| MD : Break, 50 µm | 21.0 | MPa | |
| TD : Break, 50 µm | 18.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 390 | % | |
| TD : Break, 50 µm | 510 | % | |
| Dart Drop Impact (50 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 200 | g | |
| TD : 50 µm | 240 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | 64 | ASTM D2457 | |
| Haze (50.0 µm) | 8.5 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® TP 11270 | Premix Oy | HDPE | PRE-ELEC® |
| Selvol™ E 205 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Anjacom® 350-GK30 | Almaak International GmbH | Nylon 66 | Anjacom® |
| Cellidor CP 310-08 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| POLYFORT® FPP 1876 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |