SLOVASTER® B FRN 3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Plastcom |
| Trademark: | SLOVASTER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XqVwUC_SLOVASTER-B-FRN-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT basic type for injection moulding. Melt is characterised by outstanding fludity, which enables injection moulding of complicated and divided products also on multiple moulds. Anisotropy of shrinkage enables injection moulding of round, cylindric or other hole products. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 40 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.9 | % | |
| Flow | 1.8 | % | |
| Water Content | 0.050 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 130 | kJ/m² | |
| 23°C | 130 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 55.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature (DSC) | 200 to 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 23 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ESTAPROP KM 0800 | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| ExxonMobil™ PP4712E1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Exceed™ 1018KB | ExxonMobil Chemical | mPE | Exceed™ |
| Geon™ Vinyl Flexible B5D05 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ESTOPLAST PM 1500NN01 | Ester Industries Ltd. | Acetal (POM) Copolymer | ESTOPLAST PM |