Makrolon® FR7087
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XpfmGm_Makrolon-FR7087.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 12 cm³/10 min; flame retardant; UL 94V-0/2.2 mm and 5VA/3.0 mm; medium viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320 °C; available in transparent and translucent colors; electrical/electronic |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 75.0 | MPa | |
| Break, 23°C | 75.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 5.0 | % | |
| Break, 23°C | 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength 1 | ISO 7391 | ||
| -30°C, Complete Break | 8.0 | kJ/m² | |
| 23°C, Complete Break | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 118 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 123 | °C | ISO 306/B50 |
| -- | 124 | °C | ISO 306/B120 |
| RTI Elec (1.50 mm) | 125 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 85.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 2.20 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | |
| 2.20 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 930 | °C | |
| 2.20 mm | 930 | °C | |
| 3.00 mm | 960 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 88.0 | % | ISO 13468-2 |
| Haze (3000 µm) | 0.90 | % | ISO 14782 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MFLR,(,,)-18-9 |
| Note Message | |
|---|---|
| 1 . | Based on ISO 180-A, 3 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 4011 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Quantum Composites QC-8700 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| NatureFlex™ 30NVS | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| HiFill® PC IM | Techmer Engineered Solutions | PC | HiFill® |
| Sylvin 4200-55 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |