| The Petrothene GA501 series of resins is pelletized liner low density polyethylene selected by customers for film extrusion applications that require excellent drawdown and toughness. These resins have excellent puncture resistance, elongation and heat seal strength. Typical applications include heavy duty shipping sacks, trash can liners, commercial and industrial packaging, as well as food and consumer packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested 1 | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 186 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 193 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 45.5 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 32.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 130 | g | ASTM D1922 |
| TD : 25 µm, blown film | 330 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 40 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 20 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.5:1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 232 | °C |
| Note Message | |
|---|---|
| 1 . | Blow-Up Ratio: 2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1703 Z | RTP Company | PPE | RTP |
| RAMTAL PM1429 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| Vitaster® US70WT6178 | Jackdaw Polymers | PBT | Vitaster® |
| TOTAL Polypropylene Lumicene® M 3766 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Karina GRAY COLOR CONCENTRATE 18/ 90-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |