Order Products : sales@su-jiao.com
4PROP® 9C19300
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XmGgwv_4PROP-9C19300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 9C19300 is a MFI 9 Conductive Copolymer Polypropylene |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1300 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 20.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 10 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 45.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 400 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CA70GC | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Bayfill® EA 2003 (6 pcf) | Covestro - PUR | PUR-Ether/MDI | Bayfill® |
| Boda BDF60C | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Avalon 11 | Greene, Tweed & Co. | PTFE | Avalon |
| Evoprene™ G 3294 | AlphaGary | SEBS | Evoprene™ G |