Starex NH-0925 S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XlHXc9_StarexNH0925S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex NH-0925 S is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The application areas of Starex NH-0925 S include housing and commercial/office supplies. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 6.5 | g/10 min | ASTM D1238 |
| -- | 6.5 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 105 | ASTM D785 | |
| R scale | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2200 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 41.0 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 25 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 63.0 | MPa | ASTM D790 |
| -- 8 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 190 | J/m | ASTM D256 |
| 23°C 10 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 85.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 93.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 75.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 93.0 | °C | ISO 306/B50 |
| -- | 95.0 94.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 1.5 mm | V-2 | UL 94 | |
| 2.5 mm | V-2 | UL 94 | |
| 3.0 mm | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 210 - 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 147 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3122 90/05 | MBA Polymers | PS (GPPS) | MBA PS |
| RAMLLOY PBB104 | Polyram Ram-On Industries | PC+ABS | RAMLLOY |
| Badamid® PA610 GF30 TF15 | Bada AG | Nylon 610 | Badamid® |
| Aquathene® CM04482 | LyondellBasell Industries | Proprietary | Aquathene® |
| 3M™ Dyneon™ PTFE Compound TF 3406 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |