Torayca® 3101T-30V
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torayca® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XkhvGB_Torayca-3101T-30V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torayca® 3101T-30V is a Polyamide 66 (Nylon 66) product filled with 30% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.60 | % | |
| Flow : 3.00 mm 2 | 0.20 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | % | |
| PV Limit - vs. S45C | 2.6 | MPa·m/s | Suzuki Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Amount of Wear - vs. S45C 3 | 0.600 | mg/hr | Suzuki Method |
| Coefficient of Friction - vs. S45C 4 | 0.230 | Suzuki Method | |
| Tensile Stress (23°C) | 240 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 19000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 335 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature | 265 | °C | DSC |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 1MPa, 0.33 m/s |
| 4 . | 1MPa, 0.33 m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH501G4 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| Avalon 44 | Greene, Tweed & Co. | PTFE | Avalon |
| ColorFast® PCGF110 | LTL Color Compounders, Inc. | PC | ColorFast® |
| HiFill® PPA GF33 HS L | Techmer Engineered Solutions | PPA | HiFill® |
| LUVOCOM® PEEK CLASSIX 7980 VP | LEHVOSS Group | PEEK | LUVOCOM® |