Zytel® FG77G33L NC010
| Category: | Nylon 612 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xkgmgr_Zytel-FG77G33L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% Glass Reinforced Polyamide 612 with Developed for Food Contact Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 0.30 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 1.8 | -- | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.70 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 7900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 168 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.2 | 3.2 | % | ISO 527-2 |
| Flexural Modulus | 8200 | 7000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 12 | 10 | kJ/m² | |
| -30°C | 11 | 10 | kJ/m² | |
| 23°C | 13 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 65 | kJ/m² | |
| 23°C | 80 | 90 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 11 | 10 | kJ/m² | |
| -30°C | 11 | 10 | kJ/m² | |
| 23°C | 13 | 12 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | 45 | kJ/m² | |
| 23°C | 70 | 60 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 216 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 65.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.7E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.6E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.6E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 8.3E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.6E-4 | -- | cm/cm/°C |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2130 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.26 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 GB 10 TFE 13 SI2 | RTP Company | Nylon 66 | RTP |
| NORYL GTX™ GTX679 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Bergamid™ A700 G35 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| APEX® 76-5066-H | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ THERMOCOMP™ OF008A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ THERMOCOMP™ |