ENGAGE™ 8540G
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xigdn0_ENGAGE-8540G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8540G Polyolefin Elastomer is an ethylene-octene copolymer that is well suited to foamed applications and offers excellent performance for profile extrusion of tubing and hoses. It has good clarity, toughness, and flexibility. ENGAGE 8540G also has excellent compatibility with other polyolefins, allowing for efficient blending and coextrusion. Main Characteristics:
Complies with:
Applications:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 20 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 90 | ||
| Shore D, 1 sec, Compression Molded | 47 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 9.60 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 27.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 750 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 114 | MPa | |
| 2% Secant : Compression Molded | 108 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 103 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -32.0 | °C | Internal Method |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 104 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 90.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREX TA 2150 HD | SILON s.ro | TP, Unspecified | TABOREX |
| Xuchuan XCA-4525A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Hiprolon® 11 ECN Gray H8L | Arkema | Nylon 1012 | Hiprolon® |
| Hostacom HKC 431N D72643 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ FARADEX™ MS003 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ FARADEX™ |