AKROMID® A3 S1 natural (2310)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XiVdQG_AKROMID-A3-S1-natural-2310-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 S1 natural (2310) is an unreinforced, cold impact modified polyamide 6.6 with light inherent color Applications are connectors and fixtures for the automotive electro and furniture industry, if high impact resistance at low temperatures is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.07 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 77.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.3 | -- | % | |
| Flow | 2.4 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.7 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 80.0 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | 38.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.8 | > 50 | % | |
| Break | > 50 | > 100 | % | |
| Flexural Modulus 1 | 1950 | 1000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 35 | -- | kJ/m² | |
| -30°C | 45 | -- | kJ/m² | |
| 23°C | > 80 | > 100 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | No Break | No Break | ||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 152 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 262 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min, DSC |
| 3 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X5090 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PRE-ELEC® PP 1380 | Premix Oy | TPO | PRE-ELEC® |
| Multi-Flex® TPE D3804 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| ColorFast® NY1GF130 | LTL Color Compounders, Inc. | Nylon 6 | ColorFast® |
| LNP™ STAT-LOY™ PF306 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ STAT-LOY™ |