Jampilen HP522H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XiE4EC_Jampilen-HP522H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen HP522H is a homopolymer for the production of biaxially oriented polypropylene films which is particularly suitable for metallization, both as plain film and in coextruded structures. Jampilen HP522H has been designed to provide a very stable extrusion on stenter lines and to give excellent thickness control, increased drawability and readiness to a two way orientation. This grade contains a reinforced processing stabilization but does not contain any slip or antiblocking agents and is calcium stearate free. The product features low water carry-over properties and is therefore also suitable for tubular BOPP. BOPP films produced with Jampilen HP522H feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils, fats and oxygen and good optical properties. Monolayer or coextruded films made of Jampilen HP522H with a thickness ranging from 20 to 40 µm are used for the packaging of foodstuffs, cosmetics and videocassettes.Jampilen HP522H is suitable for food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 12 | % | ASTM D638 |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| Accelerated Oven Ageing (150°C) | 500 | hr | ASTM D3012 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 0.60 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT SG5151 | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| Sinpolene CPP1020 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Iupilon® LGH2410M | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Mafill® CR XG 5544 H | Ravago Group | PP, Unspecified | Mafill® |
| Electrafil® 1105-10819 NAT | Techmer Engineered Solutions | PEEK | Electrafil® |