VECTOR 2518A
Styrene-Butadiene-Styrene (SBS) Block Copolymer

SBS(1) triblock copolymer.

Contains <1% diblock copolymer.

Medium styrene, high modulus copolymer.

Outstanding thermal stability.

Supplied as a porous pellet, dusted with talc.

VECTOR styrenic block copolymers find use under certain regulations as articles or as ingredients in articles intended for food contact or medical applications. Please contact your Dexco Polymers agent for a detailed letter of certification or further information.

VECTOR 2518A styrene-butadiene-styrene block copolymer is produced via proprietary sequential anionic polymerization technology from Dexco Polymers LP, a Dow/ExxonMobil Venture. VECTOR 2518A is not formulated with the antioxidant TNPP (tris(nonylphenyl) phosphite).

It is more creep resistant than VECTOR 8508A SBS. It has excellent thermoplastic elastomer properties and outstanding physical strength. It is designed for use as an impact/toughness modifier in blends with styrenics and in elastomeric film compounds.

General Information
Features	Copolymer Food Contact Acceptable Good Creep Resistance Good Strength Good Thermal Stability Porous
Uses	Plastics Modification
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.938	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	0.60	g/10 min	ASTM D1238
Solution Viscosity	1200	mPa·s	ASTM D2196
Ash Content	0.7	wt%	ASTM D1416
Styrene Content	31.0	wt%	Internal Method

Elastomers	Nominal Value	Unit	Test Method
Stress Relaxation ¹
Peak Force @ 200% strain (A) : 23°C, 889.0 µm	2.21	MPa
Peak Force @ 500% strain : 23°C, 889.0 µm	7.17	MPa
Ratio (A:B) : 23°C, 889.0 µm	2.20
Relaxation @ 200% strain : 23°C, 889.0 µm	5.7	%
Set after 500% strain : 23°C, 889.0 µm	16	%
Unload @ 50% strain (B) : 23°C, 889.0 µm	1.03	MPa

Additional Information	Nominal Value	Unit	Test Method
Diblock Content	< 1.0	wt%	Internal Method
Volatiles	0.3	wt%	Internal Method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 1 sec)	78		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ²(300% Strain, 25°C)	4.14	MPa	ASTM D412
Tensile Strength ³(Yield, 25°C)	30.3	MPa	ASTM D412
Tensile Elongation ⁴(Break, 25°C)	1000	%	ASTM D412

Note Message
1 .	Described in US 7,445,831 patent. Tested on roll milled/compression molded plaques (0.035" thick). Tested in the transverse direction at room temperature.
2 .	25 Wt.% in toluene
3 .	25 Wt.% in toluene
4 .	25 Wt.% in toluene

Resin Grade	Manufacturer	Category	Trademark
Torelina® A310MX04	Toray Resin Company	PPS	Torelina®
TOTAL Polyethylene XSene® HDPE XRT 70	TOTAL Refining & Chemicals	HDPE	TOTAL Polyethylene
GELOY™ XTWE265 resin	SABIC Innovative Plastics Asia Pacific	ASA	GELOY™
Edgetek™ AT-15GB/000 DFB CARBONITE	PolyOne Corporation	Acetal (POM) Copolymer	Edgetek™
Formolon® AWS	Formosa Plastics Corporation, U.S.A.	PVC, Unspecified	Formolon®